The surface carboxyl group of carbonaceous microspheres effects on the synthesis and structure of SiOC ceramics

In this study, C/SiOC and C/SiO₂ composites were prepared by using carbonaceous microspheres with different surface functional groups. Carbonaceous microspheres based on hydrothermal reaction of glucose contains hydroxyl group, while the surface carboxyl group increases after NaOH etching. The hydroxyl group increases the oxygen-enriched structural units of SiOC ceramics, and the C spheres are closely enwrapped in SiOC matrix after pyrolysis at 900 °C. However, the interfacial reaction of surface carboxyl with Si–OH results in the formation of cristobalite SiO₂, and C spheres are not only encased inside the SiOC matrix, but also dispersed outside of SiOC ceramics. After removal of C via calcination at 500 °C for 5 h, C/SiOC and C/SiO₂ composites are transformed into amorphous SiO₂ and cristobalite SiO₂, respectively. The thermogravimetric analysis indicates the oxidation resistance of SiOC is superior to that of C and SiO₂.     

一株产羧酸酯酶菌的鉴定及酯酶特征的研究

目的:鉴定中国白酒发酵过程中的微生物种类，研究关键酶的特征与作用机制有利于提高白酒的优质品率。方法:本研究用形态学和生理学、16S rRNA、gyr B基因和antiSMASH分析的方法对酒曲中的一株微生物进行了验证；对该菌株的特性进行了研究，采用分子建模的方法获得了羧酸酯酶的3D模型，用分子对接的方法探讨了该菌株的羧酸酯酶的机理。结果:该菌株为产羧酸酯酶的革兰氏阴性菌Pb1（MW580690）；该菌株呈现典型的S型生长曲线，产物曲线为S型，羧酸酯酶活化最优pH范围为5.0~9.0。分子对接结果显示Phe21A为该酶具有催化活性的主要氨基酸，水解三丁酸甘油酯为丁酸和甘油。分子对接结果显示三丁酸甘油酯经过构象变化被转移到催化中心后，进一步被加工；酶的亲水性和疏水性的相互作用表面有利于配体向下转移，进而从疏水性通道释放产物到的酶表面。结论:产羧酸酯酶的菌株为贝莱斯芽胞杆菌，并为羧酸酯酶水解三丁酸甘油酯类物质的底物识别、转移和催化机理提供了新的见解。     

Highly active sites of low spin FeⅡN4species:The identification and the ORR performance

Over recent years,catalytic materials of Fe-N-C species have been recognized being active for oxygen reduction reaction(ORR).However,the identification of active site remains challenging as it generally involves a pyrolysis process and mixed components being obtained.Herein Fe₃C/C and Fe₂N/C samples were synthesized by temperature programmed reduction of Fe precursors in 15%CH₄/H₂and pure NH₃,respectively.By acid leaching of Fe₂N/C sample,only single sites of FeN₄species were presented,providing an ideal model for identification of catalytic functions of the single sites of FeN₄in ORR.A correlation was conducted between the concentration of Fe^ⅡN₄in low spin state by Mossbauer spectra and the kinetic current density at 0.8 V in alkaline media,and such a structure-performance correlation assures the catalytic roles of low spin Fe^ⅡN₄ species as highly active sites for the ORR.     

基于统计软件R的安全壳泄漏率试验数据有效性分析

安全壳泄漏率计算过程中，最重要的环节是以不同时刻测量数据对时间进行线性回归分析。对回归的显著性检验以及方差分析是评价试验结果有效性的重要手段。本文基于统计软件R对某电厂调试阶段安全壳泄漏率试验的数据进行分析，通过对线性回归模型的独立性、正态性和异方差性检验以及极端样本点的剔除等方式，探讨泄漏率计算前的回归诊断对计算结果可靠性的影响。通过回归诊断的实例分析发现，在安全壳泄漏率计算的数据样本中，可能存在自相关、非正态和异方差性等问题影响回归结果，进而影响泄漏率的最终结果。因此，在计算泄漏率结果时，须通过回归诊断方法评价数据的有效性，对不能通过检验的样本应通过适当方法对最终结果进行修正。      

The formation of fibrous structure of polyamide 6 induced by the three-step forming process and its prominent reinforcement in nitrile rubber

Nitrile rubber (NBR) blends with excellent performance have always been a hot research topic in petroleum field. Due to the excellent performance and compatibility of polyamide 6 (PA6), it provides an opportunity for the preparation of high-performance NBR/PA6 blends. In this article, NBR/PA6 blends were prepared by the three-step molding process. Experimentally, it was found that PA6 has a prominent reinforcement effect in NBR matrix. The variation of this mechanical property was investigated from different aspects of the crystal structure, crystallinities, phase morphology, and so on. It can be cleared that the formation of fibrous structure of PA6 phase is the main factor for reinforcement of the polymer blends. Meanwhile, the formation mechanism of the special phase structure induced by the three-step process is deeply expounded and its structural evolution schematic is established. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47472.     

自然时效对GT35合金组织与性能的影响

采用XRD、SEM、残余应力测试仪、维氏硬度计、测长机等手段对合金物相、微观组织、残余应力、硬度、线膨胀率进行表征,研究自然时效对GT35合金组织与性能的影响。结果表明,GT35合金在自然时效过程中,增强相TiC的形貌与粒径没有明显变化。当自然时效时间小于15天时,GT35合金的硬度、残余应力与线膨胀率逐渐增加,随后逐渐减小并趋于稳定。当自然时效超过90天后,GT35合金的组织与性能趋于稳定,其硬度、残余应力和线膨胀率分别为945.7 HV5、-184 MPa和-2.22×10^-5。     

Effects of B2O3 on Crystallization,Structure, and Heat Transfer of CaO-Al2O3-Based Mold Fluxes

Metallurgical and Materials Transactions B - The reaction between traditional CaO-SiO2-based mold fluxes and high-Al steel inevitably changes flux composition, and, consequently, flux properties....